Mordenite (MOR) was synthesized using rice husk silica and modified by base (B), acid (A) or acid-base (AB) and converted to H-form. The modification did not destroy the MOR structure but increased surface area and generated mesopores. Lewis acidity of the parent and modified MOR samples investigated by aluminum NMR and NH3-TPD showed a decrease in the following order: HMOR > BMOR > ABMOR > AMOR. For the catalytic transformation of methylbutynol, ABMOR provided the highest conversion and selectivity of products from acid sites.

Rice husk silica (RHS) and NaY were used as supports for potassium (K) prepared from acetate buffer (B) and acetate (A) solutions. K loading did not destroy the NaY structure, but it caused a decrease in the surface area; the K species resided in micropores and on the external surface. In contrast, K loading resulted in the collapse and a decrease in the surface area of RHS. It was found that 12K/NaY-B was the most active catalyst for the transesterification of Jatropha seed oil. The minimum K content in K/NaY-B that provided complete conversion of the Jatropha seed oil was 11 wt%, and the biodiesel yield was 77.9%.

This study compared properties of silica (SiO2) from rice husk (RH) and rice husk ash (RHA) extracted by acid- and heat-treatment. The SiO2 from RH was in amorphous phase with nearly 100% purity while that from RHA was in crystalline phase with 97.56% purity. Both extracted SiO2 were used in the synthesis of zeolite NaY but that from RH was better due to the efficiency in product recovery and simplicity of extraction. After the NaY was exchanged to NH4Y and calcined to convert to HY, the product did not carry over the textural properties of the parent NaY and NH4Y.